Abstract In this study in situ bulk polymerization of L-lactide filled with layered double hydroxides (LDH) was investigated. Four different LDHs intercalated with two different organic anions (salicylate and sebacate) were synthesized and characterized. After characterization, these synthetic layered compounds were used as fillers in poly(L-lactide) (PLLA) nanocomposites with two different fillers’s loadings (1 wt% and 2 wt%). PLLA and PLLA nanocomposites were evaluated by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), ultraviolet and visible spectroscopy, thermogravimetric analysis (TGA), dynamical mechanical analysis (DMA), flexural testing and differential scanning calorimetry (DSC). The results demonstrated that, compared to PLLA, the nanocomposite containing 1 wt% of Zn/Al salicylate transmitted less UVA and UVB light, while keeping a similar transparency in the visible region. Thermogravimetric analysis revealed that the nanocomposite with 1 wt% of Zn/Al salicylate exhibited the highest thermal stability. In general the flexural and dynamical mechanical properties were reduced in compassion to neat PLLA. DSC results, demonstrated that, compared to PLLA, all the nanocomposites exhibited lower glass transition temperature and melting temperature values.

Este trabalho descreve a síntese e caracterização de nanocompósitos de poliestireno (PS) e hidróxido duplo lamelar (HDL) formado pelos cátions de ZnAl via polimerização in situ. O HDL utilizado neste trabalho foi modificado com uma mistura de dois ânions, laurato e palmitato. Para caracterização da estrutura e morfologia dos nanocompósitos sintetizados, foram realizadas análises por difração de raios X (DRX) e microscopia eletrônica de transmissão (MET). As caracterizações térmicas, mecânicas e de flamabilidade foram realizadas via análise termogravimétrica (TGA), ensaio de flexão e ensaio de flamabilidade, respectivamente. Os resultados obtidos neste trabalho sugerem que os nanocompósitos sintetizados possuem, de uma forma geral, uma morfologia intercalada/esfoliada com melhoras em suas propriedades térmicas e mecânicas, quando comparados com o PS puro. Entretanto, não foi observado melhora na propriedade de flamabilidade.

This work describes the synthesis and characterization of polystyrene (PS) and layered double hydroxide (LDH) nanocomposites formed by ZnAl cations via in situ polymerization. The LDH used in this study was modified with a mixture of two anions: laurate and palmitate. The characterization of structure and morphology for the synthesized nanocomposites was developed by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The thermal, mechanical and flammability characterizations properties were carried out via thermogravimetric analysis (TGA), bending test and flammability test, respectively. The results suggest that the nanocomposites have in general intercalated/exfoliated morphology with improvements in thermal and mechanical properties compared to the neat PS. However no significant improvement was observed on the flammability property.

Polystyrene/layered hydroxide salt (LHS) modified with sodium dodecyl sulfate was synthesized by in situ polymerization. The materials synthesized were characterized by gravimetry, X-ray diffraction (XRD), thermogravimetry analyses (TGA), differential scanning calorimetry (DSC) and the flammability test (FT). XRD demonstrated that synthesized nanocomposites in all compositions studied showed poor global dispersion of LHS in polystyrene. TGA showed a slight decrease in thermal stability. DSC curves showed that the glass transition temperature of polystyrene and nanocomposites were similar. The FT showed that the nanocomposite with low load of LHS exhibited good results.

Nanocompósitos Esfoliados de Poliestireno (PS) e Hidróxido Duplo Lamelar (HDL) composto por zinco, alumínio e dodecil sulfato de sódio, como ânion interlamelar, foram sintetizados via polimerização in situ. O efeito de diferentes composições de HDL (0,5, 1, 3 e 5% em massa) foi avaliado. Os nanocompósitos obtidos foram caracterizados através de ensaios de Difração de Raios X (DRX), Espectroscopia no Infravermelho por Transformada de Fourier (FTIR), Microscopia Eletrônica de Transmissão (MET) e Análise Termogravimétrica (TGA). Os resultados obtidos através das análises de DRX e MET mostraram que todos os nanocompósitos produzidos apresentaram morfologia esfoliada. Os resultados das TGA, quando se utilizam 50% de perda de peso como ponto para comparação, apresentaram ganhos significativos de estabilidade térmica para todas as composições dos nanocompósitos em comparação ao poliestireno puro. Este comportamento possibilita uma vasta gama de aplicação destes novos materiais em diversos campos da indústria e pesquisa.

Exfoliated nanocomposites of polystyrene (PS) and layered double hydroxide (LDH) compound of zinc, aluminium and sodium dodecyl sulfate, as interlayer anion, have been synthesized via in situ polymerization. The effect from the LDH compositions (0.5, 1, 3, 5% weight) was studied. The nanocomposites were characterized by X-ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), Transmission Electron Microscopy (TEM) and Thermogravimetric Analysis (TGA). The XRD and TEM results showed an exfoliated morphology for the nanocomposites in all compositions. With the 50% weight loss taken as a reference, the TGA results indicated significant improvement in thermal stability for all compositions of the nanocomposites, in comparison to pure polystyrene. This is promising for the application of these new materials in many fields of industry and research.