Abstract Aim: To evaluate the long-term post push-out bond strength to dentin, water sorption, solubility and swelling of conventional and self-adhesive dual-cure resin cements. Methods: Forty-eight bovine roots were prepared for fiber post cementation with RelyX ARC and RelyX U100. According to resin cement and storage time (24 h and 6 months), 4 groups were assessed using the push-out test. Water sorption and solubility were performed according to ISO 4049:2009. The swelling coefficient was obtained using cement disks of each material immersed in distilled water until the swelling equilibrium was reached. The mass of dry and swelled polymer and solvent density were used to calculate the coefficient. Statistical data analysis was performed using Student's t-test for water sorption, solubility and swelling coefficient and the Kruskal-Wallis and Dunn multiple comparison tests for push-out analysis with a significance level of 0.05. Results: The immediate bond strength was not significantly different between RelyX ARC (3.09 MPa) and RelyX U100 (3.78 MPa) (p>0.05). RelyX U100 showed higher (p<0.05) bond strength after six months of storage (9.60 MPa) than RelyX ARC (6.65 MPa). The water sorption and solubility values were not significantly different (p>0.05) between groups. The swelling coefficient of the RelyX U100 group was significantly higher than that of the RelyX ARC group (p<0.05). Conclusions: RelyX U100 resin cement showed a higher swelling coefficient than RelyX ARC, and the longitudinal push-out bond strength increased after six months. Clinical significance: The clinical longevity of restorative treatment in root-filled teeth is dependent on the long-term properties and behavior of the cement used for post luting. Results of this study suggest that the selfadhesive resin cement may be a reliable alternative.

The aim of this study was to evaluate the physical properties of irreversible hydrocolloid materials poured immediately and after different storage periods. Four alginates were tested: Color Change (Cavex); Hydrogum (Zhermack); Hydrogum 5 (Zhermack); and Hydro Print Premium (Coltene). Their physical properties, including the recovery from deformation (n = 3), compressive strength (n = 3), and detail reproduction and gypsum compatibility (n = 3), were analyzed according to ANSI/ADA specification no. 18. Specimens were stored at 23ºC and humidity and were then poured with gypsum immediately and after 1, 2, 3, 4, and 5 days. The data were analyzed by two-way analysis of variance (ANOVA) and Tukey's test at p < 0.05. All of the alginate impression materials tested exhibited detail reproduction and gypsum compatibility at all times. Hydro Print Premium and Hydrogum 5 showed recovery from deformation, as established by ANSI/ADA specification no. 18, after 5 days of storage. As the storage time increased, the compressive strength values also increased. Considering the properties of compounds' recovery from deformation, compressive strength, and detail reproduction and gypsum compatibility, irreversible hydrocolloids should be poured immediately.