ABSTRACT Activated carbons (AC) are high porosity and adsorptive carbonaceous materials. These adsorbents can be produced using different organic materials. Precursor material properties may impact their quality. This study aimed to produce activated carbon from Tectona grandis wood wastes, besides determining efficiency in adsorption of different pollutants. Chemical activation, with ZnCl2 (AC_ZnCl2) and CuSO4 (AC_CuSO4), and physical activation, with CO2 (AC_CO2) were performed. Activated carbons were characterized by FTIR, surface functional groups (Boehm) and surface area analysis. Moreover, ACs were tested regarding adsorption capacity of methylene blue (MB), phenol and Cr+6 ions in aqueous medium. Higher total pore volume (0.62 cm³ g-¹), micropore volume (0.31 cm³ g-¹) and surface area (524.50 m² g-¹) were obtained in AC_ZnCl2, which was also the most effective in MB and phenol adsorption. AC_CuSO4 obtained high adsorption capacity for phenol and presented functional groups different from the other AC. AC_CO2 was the second with better adsorption performance for all pollutants.

ABSTRACT The non-structural carbon reserves in the various organs of trees are associated with their growth and the mechanism of resilience when exposed to environmental stresses, especially the water deficit. The goal of this study was to develop multivariate models to estimate the amount of non-structural carbohydrates (starch, sucrose, reducing sugars, total sugars and total non-structural carbohydrates) based on near infrared (NIR) spectra measured in solid wood and material reduced to powder. Partial least squares regression was used to associate the amount of non-structural carbohydrates (NSC) obtained by conventional laboratory analysis with NIR spectral signatures. The best predictive models were obtained from the wood reduced to powder. Validity for the NSC prediction in an external set of data presented the following statistics: reducing sugars with R²=0.90 and root mean square error (RMSE) of 2.54% dry matter, total sugars (R²=0.88, RMSE=2.76%), total NSC (R²=0.90, RMSE=2.58%), sucrose (R²=0.82, RMSE=0.06%) and starch (R²=0.80, RMSE=1.03%). The ability of models to estimate the NSC concentration in the growth rings and under divergent environmental conditions demonstrates the potential of the NIR tool to study the physiological responses of plants to different environmental stresses.

ABSTRACT Currently, there is a little and sparse information about how the growing conditions influence the spatial variation of wood along the stem. Thus, the aim of this study was to compile the knowledge from literature in a manuscript for better understanding to what extent the growing conditions influence the spatial variation of wood properties in Eucalyptus plantations. The wood characteristics may present variations in their properties and can be caused by both genetic and environmental factors. However, how genetic and environmental factor acts on wood variation along the trunk is still unclear. Another point is that even with new genetic breeding programs, the mechanical properties of wood have not been considered in these programs, since the selection of new material is always based on the growing rate, cellulose and lignin content and wood density.

ABSTRACT This study aimed to evaluate the behavior of samples of juvenile and mature Eucalyptus cloeziana wood when subjected to the drying process, and the influence of the anatomy on that behavior. In order to do this, saturated specimens from this woods measuring 10 × 5 × 1 cm were subjected to drastic drying at 100 °C, where the drying rates and the end check scores in different steps of the process were obtained. The fibers and vessels morphology, initial moisture and basic density were analyzed to help understanding the data obtained in the drying test. The juvenile wood presented 26% higher drying rate and 21% smaller drying time, also 53% higher end check score. Smaller fibers length and fibers wall thickness, higher vessels frequency and smaller vessels diameter were associated with higher total drying rate and water adsorption, as well as with the higher end check score.

ABSTRACT The objective of this study was to establish the correlation between the size of the wood knots and the modulus of elasticity (MOE) and the compressive strength (Fc) in Eucalyptus wood. 156 Eucalyptus urophylla samples with knots were separated into 3 classes (small, medium and large knots), and samples were selected from the same tree and submitted to the parallel fiber compression test for MOE and Fc determination. There was a significant difference between the MOE and Fc of the smaller knot class (Class 1) and the other classes with larger knots (Classes 2 and 3). In general, the larger the knot, the greater the difference between the MOE and Fc. Wood with small knots (8.31 mm2) presents stiffness and strength statistically equal to wood free of defects. Eucalyptus wood stiffness is more sensitive to the presence of knots than the strength when compared to clear wood samples.

This work describes the chemical composition of the volatile oil of Hyptis marrubioides cultivated in field and greenhouse. The experimental design was completely randomized, with ten replications for each type of cultivation. The volatile oil was extracted by hydrodistillation and analyzed by GC-MS. The highest content of volatile oil was found for plants grown in field. The highest percentage of the compounds present in oils was observed in samples grown in the field, such as germacra-4(15),5,10(14)-trien-1-α-ol (16.34%), β-caryophyllene (10.42%), γ-muurolene (12.83%) and trans-thujone (9.98%). However, some compounds were found only in plants grown in a greenhouse, such as cis-muurol-5-en-4α-ol (10.84%), α-cadinol (3.06%) and eudesma-4(15),7-dien-1β-ol (6.82%).