ABSTRACT Radar absorbing materials (RAMs) are composites made with a polymeric matrix and an electromagnetic absorbing filler, such as carbon black (CB), silicon carbide (SiC) or manganese zinc ferrite (MnZn). To enhance their performances to attenuate an incident wave through reflection loss (RL), RAMs can be produced in multilayer structures. Usually, the RL analysis is done theoretically and experimentally validated with free space analysis. Here, it was demonstrated that multilayer structure can be designed and easily validated using rectangular waveguide, using a simpler setup and small samples. Three composites were produced using 2 wt% of CB (CB2), 40 wt% of SiC (SiC40) and 60 wt% of MnZn (MnZn60). They were characterized over the Ku-band and used to validate the multilayer structures, that were prepared by simply stacking each material inside the waveguide sample holder. One of the best results was obtained with structure SiC40+CB2 with 5.85 mm thickness, that presented a calculated RL of -21 dB at 17.8 GHz and a measured RL of -36 dB at the same frequency. In conclusion, using rectangular waveguide has been proven to be an easy, cheap, precise and fast approach to validate multilayer structures designs.

ABSTRACT This contribution reports the use of an organic gel, xerogel, as catalyst support for Cu. The xerogel was synthesized from the system tannin-formaldehyde at pH 3, using F-127 Pluronic as surfactant. The surface area values were higher than 900 m2/g even after the Cu (10%, wt) impregnation. The morphological analysis by SEM-FEG revealed the presence of spheres arranged in a tridimensional structure. XRD diffractograms showed the presence of CuO and Cu2O crystalline phases combined with the amorphous structure of the porous carbon. From XRD analysis it is possible to infer the Cu species are heterogeneously dispersed on the support with the co-existence of small and larger clusters, which is in agreement with Raman spectroscopy. Raman study also indicated a highly defect/disorder structure of the xerogel derivatives, ensuing the short-range structural order of the carbonic structure and oxygen groups decorating the carbon surface. XPS results corroborate with XRD and Raman results, detecting the presence of CuO and Cu2O. In addition to the mentioned Cu species, XPS also detected Cu0 which may be originated from the chemical interaction between the electron oxygen groups with the Cu precursor. The high surface area and the thermal stability (~ 300 ºC) of Cu/XCTF envisages its feasibly for relevant catalytic applications.

ABSTRACT Radar Absorbing Materials (RAMs) are composite materials able to attenuate an incident electromagnetic wave. Usually, RAMs are made of a polymeric matrix and an electromagnetic absorbent filler, such as silicon carbide or carbon black. Several materials have been investigated as potential fillers, aiming to improve the Reflection Loss (RL) and absorption bandwidth broadening. In this paper, a composite made with silicone rubber and biochar was investigated as a sustainable porous carbon made with biomass waste. Five different composites were characterized, composed of 1 - 5 wt.% of biochar in the silicone rubber. Although the RL of pure biochar composites is not significant, it was demonstrated here how a biochar composite can improve the RL of a RAM material when it is applied as a double-layer structure. While the RL of a ferrite-based RAM with 2.0 mm thickness reaches -28 dB, a combination of this RAM with biochar composite reaches ~ -60 dB with the same thickness. The double-layer structure with 2.3 mm thickness can have an absorption bandwidth of 2.95 GHz over the X-band frequency range, and a structure with 2.6 mm thickness can reach a RL of ~ -76 dB. This demonstrates a sustainable, cheaper, and lighter material application (i.e., biochar), which is successfully used in the development of high-efficient electromagnetic shield or sensors.

RESUMO Este trabalho apresenta as propriedades eletromagnéticas de um Material Absorvedor de Radiação Eletromagnética (MARE) feito a partir de Carbeto de Silício (SiC) e Negro de Fumo (NF) como aditivos. O compósito SiC/NF foi produzido utilizando 70 %(m/m) de matriz de silicone, e variando as concentrações do aditivo em 3 %(m/m), 2 %(m/m) e 1 %(m/m) de NF com 27 %(m/m), 28 %(m/m) e 29 %(m/m) de SiC, respectivamente. A estrutura química e a morfologia das partículas de SiC e NF foram analisadas através de espectroscopia Raman e Microscopia Eletrônica de Varredura (MEV). As propriedades dielétricas dos MAREs foram obtidas por meio do analisador de rede vetorial na faixa de frequência de 12,4 a 18,0 GHz. Os resultados de refletividade mostraram que o compósito SiC/NF com 1 %(m/m) de NF apresentou a melhor absorção de radiação eletromagnética, chegando a -47,9 dB em 16,8 GHz com uma amostra de aproximadamente 5,5 mm de espessura.

ABSTRACT Este trabalho apresenta as propriedades eletromagnéticas de um Material Absorvedor de Radiação Eletromagnética (MARE) feito a partir de Carbeto de Silício (SiC) e Negro de Fumo (NF) como aditivos. O compósito SiC/NF foi produzido utilizando 70 %(m/m) de matriz de silicone, e variando as concentrações do aditivo em 3 %(m/m), 2 %(m/m) e 1 %(m/m) de NF com 27 %(m/m), 28 %(m/m) e 29 %(m/m) de SiC, respectivamente. A estrutura química e a morfologia das partículas de SiC e NF foram analisadas através de espectroscopia Raman e Microscopia Eletrônica de Varredura (MEV). As propriedades dielétricas dos MAREs foram obtidas por meio do analisador de rede vetorial na faixa de frequência de 12,4 a 18,0 GHz. Os resultados de refletividade mostraram que o compósito SiC/NF com 1 %(m/m) de NF apresentou a melhor absorção de radiação eletromagnética, chegando a -47,9 dB em 16,8 GHz com uma amostra de aproximadamente 5,5 mm de espessura.

In this manuscript, the electromagnetic wave absorption properties of sustainable porous carbon composites were evaluated over the X-band frequency range (8.2 - 12.4 GHz). The porous carbon material was made from the byproduct of cellulose production and was used as additive on the development of radar absorbing material (RAM) composites. These porous carbon materials have different characteristics, such as porosity size (180 µm < Ø1 < 250 µm and 425 µm < Ø2 < 500 µm) and particle size (ϕ1 < 250 µm and 250 µm < ϕ2 < 425 µm). Composite materials were also studied as frequency selective surface (FSS) structures. It was shown how complex permittivity and reflection loss (RL) can be manipulated over the frequency range using FSS structure. While regular RAM presented RL of 19 dB at ~11.8 GHz, FSS structure presented a RL of 19 dB shifted to 12.4 GHz regarding the same carbon porous material (with particles between 250 and 425 µm and porosity between 180 and 250 µm). It was demonstrated here the potential use of sustainable porous carbon as RAM, and how FSS structure can be used to tune the frequency of the RL maximum peak.