O objetivo deste trabalho foi avaliar o potencial de resíduos de madeira de quatro espécies amazônicas para fins energéticos, além de calibrar propriedades da madeira e do carvão vegetal utilizando a técnica NIRS. Foram utilizadas costaneiras das espécies cardeiro (Scleronema micranthum Ducke), cedrinho (Scleronema sp.), louro (Ocotea sp.) e piquiarana (Caryocar villosum Pers.), tendo sido determinadas as seguintes propriedades: densidade básica, composição química, análise química imediata e poder calorífico superior da madeira; rendimentos em carvão vegetal; análise química imediata, poder calorífico e friabilidade do carvão vegetal. Foram adquiridos espectros NIR e gerados modelos para calibração de cada propriedade energética. Os resultados indicam que todas as espécies possuem potencial como fonte bioenergética. Entretanto, as melhores espécies foram o cardeiro e o piquiarana, devido à maior densidade básica e energética, além do louro, com maior teor de lignina e carbono fixo, que apresentou, consequentemente, maior poder calorífico. A espectroscopia NIR mostrou-se como uma ferramenta possível para calibração de propriedades energéticas da biomassa.

The aim of this study was to evaluate the energy-related potential of wood residues of four Amazonian species and calibrate the properties of wood and charcoal using the Near Infrared Spectrometry (NIRS) technique. Residue slabs of cardeiro (Scleronema micranthum Ducke), cedrinho (Scleronema sp.), louro (Ocotea sp.), and piquiarana (Caryocar villosum Pers.) wood were used. The following properties were determined: density, chemical composition, immediate chemical analysis, and superior calorific value of wood; and yield, immediate chemical analysis, calorific value, and friability of charcoal. NIR spectra were obtained and calibration models were generated for each energy property. The results indicate that residues of these forest species can be used as a renewable energy source. NIR spectroscopy has proved to be a possible tool for calibrating energy properties of wood.

RESUMO O objetivo deste estudo foi avaliar o efeito da adição da farinha de babaçu nas propriedades do adesivo à base de ureia-formaldeído e compará-lo ao adesivo produzido com farinha de trigo, extensor usualmente utilizado na produção de painéis compensados. À resina ureia-formaldeído foram adicionados, em partes por massa de adesivo, 0, 10, 20 e 30% de farinha de babaçu, e, como catalisador, sulfato de amônio, na proporção de 1,5% sobre a massa seca de sólidos da resina. Determinaram-se as seguintes propriedades dos adesivos: viscosidade, teor de sólidos, tempo de gelatinização, tempo de trabalho e pH. A farinha de babaçu apresentou propriedades semelhantes às da farinha de trigo. Ambas, de modo geral, embora tenham contribuído para o aumento da viscosidade dos adesivos, reduziram sua reatividade, pois elevaram o valor pH, o tempo de gelatinização e o tempo de trabalho.

ABSTRACT The aim of this study was to evaluate the effect of the addition of babaçu flour on urea-formaldehyde adhesive properties and compare it to the adhesives produced with wheat flour, which is the extender usually used for plywood production. An amount of 0, 10, 20 and 30 parts of extender per weight of the adhesive were added. Ammonium sulfate was used as catalyst, in the proportion of 1.5% on dry weight of solid content. The following properties of the adhesive were determined: viscosity, nonvolatile content, gel time, working life and pH. The babaçu flour presented similar properties to wheat flour. Both, in general, although contributed to the increase of the adhesives viscosity, reduced its reactivity, as increased pH value, gel time and working life.

Neste trabalho, objetivou-se avaliar a qualidade da colagem de painéis compensados de Pinus taeda, produzidos com resina fenol-formaldeido de alto e baixo peso molecular, e lâminas de três diferentes classes de densidades. O experimento foi organizado em seis tratamentos, e para cada tratamento foram produzidos três painéis (repetições). Os ensaios de resistência da linha de cola aos esforços de cisalhamento foram realizados após dois ciclos de fervura e após 24 horas de imersão em água fria. Determinou-se, também, a porcentagem de falhas na madeira. Os resultados indicaram que as classes de densidade são estatisticamente diferentes entre si. Entretanto, não houve diferença significativa entre os valores médios de resistência da linha de cola dos painéis produzidos com resina de alto e baixo peso molecular, tanto para os painéis submetidos aos dois ciclos de fervura, quanto para os submetidos ao ensaio após 24 horas em água fria. A interação entre as classes de densidade das lâminas e as formulações do adesivo, igualmente, não foi significativa. A resina de baixo peso molecular (BPM) e os compensados produzidos com as lâminas de maior densidade apresentou melhor comportamento, tanto para resistência quanto para a porcentagem de falha na madeira. Conclui-se que a qualidade de colagem dos painéis compensados de Pinus taeda produzidos com lâminas de densidades diferentes e com resinas fenólicas de alto e baixo peso molecular foi satisfatória. Todos os tratamentos atendem às exigências mínimas da norma européia EN 314-1/1993, que trata da qualidade da colagem de painéis compensados.

This study aimed to evaluate the bonding quality of plywood panels from Pinus taeda using low and high molecular weight phenol-formaldehyde resin and veneers from three different density classes. The experiment consisted of six treatments, each of which produced three panels (replicates). Tests were conducted to evaluate glue line strength to shear stress after two boiling cycles and after 24 hours of cold water immersion. Also determined was the percentage of defects in wood samples. Results indicated that the density classes being assessed differed statistically. However, no significant difference was found between panels produced with high and panels produced with low molecular weight resin as to the mean values of glue line strength, whether subjecting them to two boiling cycles or after 24 hours of cold water immersion. Interactions between different density classes and adhesive formulations were found not significant either. Low molecular weight resin (BPM) and panels produced with higher density veneers were found to have better behavior, regarding both bonding strength and percentage of defects. It was concluded that the bonding quality of plywood panels from Pinus taeda was satisfactory after using different densities of veneer and also high and low molecular weight phenolic resins. All treatments were found to comply with minimum requirements established in European standard EN 314-1/1993, which addresses bonding quality of plywood panels.

Esta pesquisa teve como objetivo avaliar a qualidade de painéis aglomerados produzidos com resíduos de processamento em serraria de nove espécies de madeiras tropicais da Amazônia. As espécies estudadas foram: Scleronema micranthum Ducke (Cardeiro), Ecclinusa guianensis Eyma (Caucho), Scleronema sp. (Castanha-de-paca), Copaifera multijuga Hayne (Copaíba), Ocotea sp. (Louro), Ocotea guianensis Aubl (Louro-espinho), Caryocar villosum Pers. (Piquiarana), Couratari oblongifolia Ducke & R. Knuth (Tauari) e Virola surinamensis Rol. Warb (Virola). Foram produzidos painéis experimentais com densidade nominal de 0,75 g.cm-3, utilizando a resina uréia-formaldeído na proporção de 8% de sólidos - base peso seco das partículas. Os painéis foram prensados com pressão específica de 4,0 MPa, temperatura de 160 ºC e tempo de prensagem de oito minutos. As avaliações dos resultados de ensaios obtidos nesta pesquisa indicam a viabilidade técnica de utilização das nove espécies provenientes de florestas tropicais da Amazônia na produção de painéis de madeira aglomerada, com destaque para Ecclinusa guianensis Eyma (Caucho) que, de uma forma geral, apresentou melhores resultados de propriedades físico-mecânicas.

This research was developed to evaluate the quality of particleboards manufactured from sawmill waste of nine tropical wood species of Amazônia. The following species were studied: Scleronema micranthum Ducke (Cardeiro), Ecclinusa guianensis Eyma (Caucho), Scleronema sp. (Castanha-de-paca), Copaifera multijuga Hayne (Copaíba), Ocotea sp. (Louro), Ocotea guianensis Aubl (Louro-espinho), Caryocar villosum Pers. (Piquiarana), Couratari oblongifolia (Tauari) e Virola surinamensis Rol. Warb (Virola). The experimental boards were manufactured with the nominal density of 0.75 g.cm-3, using the urea-formaldehyde resin in the proportion of 8% of solid content based on oven dried wood particles. The boards were pressed at the specific pressure of 40 kgf/cm², temperature of 160 ºC and press time of eight minutes. The evaluations of test results obtained in this study indicate the potential use of the nine species from Amazon rainforest in the production of particleboard, highlighting Ecclinusa guianensis (Caucho) that, in general, showed better results of physical and mechanical properties.

Objetivou-se, nesta pesquisa, avaliar a qualidade dos painéis laminados unidirecionais (LVL) produzidos com lâminas de Schizolobium amazonicum (paricá), Eucalyptus saligna e Pinus taeda. Foram produzidos em laboratório painéis LVL com sete lâminas de 2,0 mm de espessura com diferentes composições utilizando resina fenol-formaldeído. As lâminas de paricá foram préclassificadas em diferentes classes de módulo de elasticidade dinâmico (MOEd) através do uso de "stress wave machine". As lâminas de Eucalyptus saligna e Pinus taeda foram utilizadas nas capas dos painéis com objetivo de reforçar a resistência estrutural dos painéis LVL. Foram avaliadas as propriedades de resistência da linha de cola aos esforços de cisalhamento (RLC) e flexão estática (MOE e MOR, edge e flat). A classificação de lâminas de paricá com base nas classes de MOEd não influenciou de forma significativa nos resultados de resistência da linha de cola, MOE e MOR edge. Para o MOE e MOR flat, a utilização de lâminas com MOEd classe 1, contribuiu de forma significativa para o aumento nos valores médios destas propriedades. Da mesma forma, a utilização de lâminas de Eucalyptus saligna nas faces do painel contribuiu para o aumento nos valores médios de MOE e MOR, edge e flat.

This research evaluated the quality of laminated veneer lumber -LVL manufactured with veneers of Schizolobium amazonicum (paricá), Eucalyptus saligna and Pinus taeda. The LVL panels were manufactured in the laboratory conditions composed by seven veneers, 2,0 mm thickness, with different structural compositions, using phenol-formaldehyde resin. The veneers of Schizolobium amazonicum- paricá- were pre-classified by using stress wave machine. The veneers of Eucalyptus saligna and Pinus taeda were disposed in the face layer to reinforce the structural strength of LVL panels. The LVL quality was evaluated using glue line shear strength and static bending test (MOE and MOR, edge and flat). Grading of paricá veneers based on MOEd did not affected significantly the results of the glue line shear strength and MOE and MOR edge. For the MOE and MOR flat, the use of veneers of MOEd grade 1 contributed significantly to increasing the average values of these properties. In the same way, using the Eucalyptus saligna veneers on the face of LVL resulted in higher average values of MOE and MOR, edge and flat.