This work presents an evolution profile of labels and containers of commercial chemicals employed in laboratories since 1870. Most chemicals were made in Germany before the Second World War, after which many other manufacturers arrived on the Brazilian market. North-american products were dominant in the 1940s, but Brazilian chemicals have increased their participation along time. Labels presented increasingly more information, from originally simple names of the compounds at the beginning of the XXth century to the data presented today such as chemical formulae, safety regards and detailed chemical analysis. The raw material for container manufacturing also changed: glass was dominant until the 1950s, but nowadays plastic flasks are preferred whenever possible. Cork covers were replaced by screw caps. The diversity of commercial products also sharply increased with time, especially after the 1950s, following the many new and specific applications of chemicals for research and commercial purposes.

Samples of copper compounds covering all of the XXth century and the end of the XIXth century were submitted to classical and instrumental quantitative analysis. The amount of impurities greatly decreased with time, reaching a constant level since the 1960's. The gravimetric method was suitable for the determination of copper although other procedures also gave good or reasonable results. However, for metal contaminants, atomic absorption spectrometry was the best choice because of its lower detection limits, being able to determine several elements in the oldest samples. Ion chromatography detected several anions in copper salts manufactured before the 1950's. An increasing quality of raw materials and a better sensitivity of analytical methods led to quality improvement of copper compounds with time.

Pyro and hydrometallurgical processes were applied to the treatment of spent commercial zeolites (a molecular sieve and a ZSM-5 sample). Both catalysts were employed in pilot plant units. They were kept in their original shape, they were not regenerated and were not subjected neither to mechanical stress nor to overheating zones during their time on-stream. Two recycling processes were tested: (i) direct solubilization of samples in mixtures of HF + H2O2 (60 ºC, 1 h). Although silicon was solubilized, insoluble matter was found in both samples, particularly in the molecular sieve, due to its high amounts of alkaline and alkaline-earth metals; (ii) fusion with KHSO4 (5 h, 600 ºC) with KHSO4/zeolite mass ratio 6:1. After fusion the solid was solubilized in water (100 ºC), leaving silicon as SiO2 residue. In both processes, solubilized metals were isolated by conventional selective precipitation techniques. Analysis of final products by common analytical methods shows that metals present in the original catalysts were recovered with very high yields except when the molecular sieve was treated with HF + H2O2. This reactant mixture proved to be suitable for processing zeolites with a low alkaline and alkaline-earth metal content whereas fusion with KHSO4 appeared to be adequate for all types of zeolites.