Abstract This work investigates the effect of eco-friendly chemical treatments on the mechanical and physical properties of composite laminates based on sisal fibres. A 2231 full-factorial design is conducted to test the influence of chemical solution types, fibre treatment time, and polymer matrix type on the mechanical and morphological characterisation of the composites. Chemical treatments remove impurities from fibre surfaces, and enhance fibre-matrix adhesion. The treatments, especially with sodium carbonate (Na2CO3), also progressively reduce the hemicellulose fibre content. Polyester composites made with sisal fibres treated with Na2CO3 for 96h achieve enhanced strength and stiffness under tensile, compressive and impact loads. The results evidence the feasibility and efficiency of the proposed eco-friendly treatments for natural fibres and the application of renewable fibre laminates in secondary structural applications.

The development of new materials based on industrial wastes has been the focus of much research for a sustainable world. The growing demand for tyres has been every year exacerbating environmental problems due to indiscriminate disposal in the nature, making a potentially harmful waste to public health. The incorporation of rubber particles from scrap tyres into polymeric composites has achieved high toughness and moderate mechanical properties. This work investigates the geometric effects (thickness, width and internal cell angle) of auxetic structures made of recycled rubber composites based on experimental and numerical data. The response surface models integrated with the swarm intelligence and finite element analysis were proposed in order to obtain a range of solutions that provides useful information to the user during the selection of geometric parameters for reentrant cells. The results revealed the cell thickness ranges from 39-40 mm and 5.98-6 mm, and the cell angle range from -0.01 to -0.06º maximize the ultimate strength. The same parameters were able to optimize the modulus of elasticity of rubber auxetic structures, excepting for the angle factor which must be set between -30º and 27.7º. The optimal Poisson's ratio was found when the cell angle ranged from -30º to -28.5º, cell width ranged from 5-5.6 mm and 2 mm in thickness.