In this study, MAO treatment was used to enrich, with bioactive Ca, Mg and P atoms, as-casted and heat-treated Ti-15Zr-xMo (x = 0, 5, 10 and 15 wt%) alloys, for potential use as advanced metallic biomaterials. The chemical composition of the surface was evaluated by EDS and XPS measurements. The morphology and microstructure was analyzed by OM and SEM images. Crystalline structure and phase composition were characterized by XRD measurements. The results indicated that the oxide layers were porous, with microstructural features of the bulk (grain size and secondary phases) slightly affecting the surface characteristics (pore size, chemical and phase composition). The crystalline structure of the oxide layers were composed by a mixture of anatase and rutile phases (TiO2), with a minority of tetragonal zirconia (ZrO2) and traces of CaCO3 and P2O3 compounds. Chemical analysis indicated that the oxide layers were composed mainly by Ti and Zr oxides, with successful incorporation of the bioactive elements. The obtained results evidenced that the surface characteristics of MAO-treated Ti surfaces can be properly adjusted by the addition of alloying elements and implementation of specific heat treatments on the substrate. This finding can be quite useful for the development of novel biomedical implants.

The development of hybrids materials has been extensively investigated in recent years. The combination of a wide variety of compositions and production processes had permitted the use of these materials in different applications like coatings for corrosion protection of metals. In this work organic-inorganic hybrid materials have been prepared from the hydrolysis of tetraethylorthosilicate and silanol-terminated polidymetilmetoxysilane using a sol-gel process. These materials have been applied on galvanized steel and on steel electroplated with a ZnFe. In order to evaluate the degradation behavior of these coatings, electrochemical techniques (Electrochemical Impedance Spectroscopy and Potentiodynamic Polarization) were used. EIS data was fitted to an equivalent circuit from which the electrochemical parameters were obtained. Results show a good protective character of the hybrid films, when compared with uncovered specimens. The overall performance of the coating systems appears to be highly dependent on the kind of metallic coating applied to the steel.

In the field of biomedical applications a special interest exists regarding the study of the physicochemical and mechanical behaviour of materials, with special focus on the electrochemical degradation of metal/ceramic interfaces. In fact, metal/ceramic interfaces may be present in several biomedical devices, ranging from external or implantable sensors, to dental implants. Diffusion bonding represents an important technique since, in opposition to other production technologies, such as active metal brazing, avoid the possible liberation of certain chemical components harmful to health. The aim of this work is to study the electrochemical degradation of the interface formed between commercially pure Ti and Al2O3 produced by diffusion bonding, in contact with a physiological solution. The present approach included the evaluation of the contribution of individual and pairs of interfacial layers on the global degradation processes. For this propose d.c. electrochemical techniques were used to monitor the open-circuit potential, and to perform potentiodynamic polarization and galvanic corrosion evaluation. Also, electrochemical impedance spectroscopy was used as a complementary technique of the corrosion behaviour of the interface. Chemical composition and morphology of samples and corrosion products were evaluated by SEM and EDS analysis. According to experimental results, two principal reaction layers were formed in the interface: TiAl and Ti3Al. The TiAl layer appears to be the responsible for the strong increase in corrosion rate of the interface.