Abstract Bovine pericardium (BP) has been used as a biomaterial for several decades in many medical applications particularly due to its mechanical properties and the high collagen content. In the acellular form it favors faster tissue repair, providing a three-dimensional support for cellular and vascular events observed during tissue repair and due, to a low elastin content, may favor its use as a breast implant cover, resulting in a low possibility of contracture of the biomaterial, preventing the appearance of irregularities during the reconstruction process. Thus, the aim of this study was to evaluate, histomorphologically, the behavior of acellularized bovine pericardium (ABP) as a mammary implant cover in rats. For this purpose, 16 animals were divided into two groups, with eight animals at each biological point: 7 and 15 days after surgery. Of the 16 animals, 32 specimens were obtained: 16 in the experimental group (EG) and 16 in the control group (CG). Throughout this study, none of the studied groups had postoperative complications. Results: The histomorphological results showed, in the two biological points, both in the EG and in the CG, chronic inflammatory infiltrate, leukocyte fibrin exudate, formation of granulation tissue and deposition of collagen fibers, more evident in the EG, regressive along the biological points. At 15 days, the implanted ABP showed initial biointegration with the fibrous capsule and surrounding tissues of the recipient bed. Conclusion: These results indicate that the due to the observed favorable tissue response ABP may be of potential use as a breast implant cover.

Resumo O pericárdio bovino (PB) tem sido utilizado como biomaterial há várias décadas em diversas aplicações médicas, principalmente devido às suas propriedades mecânicas e ao alto teor de colágeno. Na forma acelular, favorece a reparação tecidual mais rápida, dando um suporte tridimensional para eventos celulares e vasculares observados durante a reparação tecidual e devido ao baixo teor de elastina, pode favorecer seu uso como cobertura de implantes mamários, resultando em baixa possibilidade de contratura do biomaterial, evitando o aparecimento de irregularidades durante o processo de reconstrução. Assim, o objetivo deste estudo foi avaliar, histomorfologicamente, o comportamento do pericárdio bovino acelularizado (PBA) como cobertura de implante mamário em ratos. Dezesseis animais foram divididos em dois grupos, com oito animais em cada ponto biológico: 7 e 15 dias após a cirurgia. Dos 16 animais, 32 espécimes foram obtidos: 16 no grupo experimental (GE) e 16 no grupo controle (GC). Ao longo deste estudo, nenhum dos grupos estudados apresentou complicações pós-operatórias. Os achados histomorfológicos mostraram, nos dois pontos biológicos, tanto no GE quanto no GC, infiltrado inflamatório crônico, exsudato fibrino leucocitário, formação de tecido de granulação e deposição de fibras colágenas, mais evidentes no GE, regressivas ao longo dos pontos biológicos. Aos 15 dias, o PBA implantado apresentou biointegração inicial com a cápsula fibrosa e tecidos circundantes do leito receptor. Esses resultados indicam que, devido à resposta favorável do tecido observado, o PBA pode ser de uso potencial como cobertura de implante mamário.

Resumo O objetivo deste estudo foi analisar o comportamento biológico de microesferas de hidroxiapatita (HA) substituída com magnésio (Mg) durante o reparo de defeito ósseo crítico, tendo em vista que este íon é de grande interesse clínico, pois está intimamente associado à homeostasia e à mineralização óssea. Para tanto, utilizou-se 30 ratos para compor três grupos experimentais: GI - defeito ósseo preenchido com microesferas de HA; GII - defeito ósseo preenchido com microesferas de HA substituída com Mg; GIII (controle) - defeito ósseo vazio; avaliados nos pontos biológicos de 15 e 45 dias. Os resultados histológicos evidenciaram, aos 15 dias, discreto infiltrado inflamatório crônico e neoformação óssea restrita às bordas, em todos os grupos. Nos grupos GI e GII, os biomateriais mantiveram-se íntegros e circundados por tecido conjuntivo frouxo. Aos 45 dias, notou-se resposta inflamatória do tipo crônica granulomatosa discreta nos grupos GI e GII, e no GIII presença escassa de células inflamatórias mononucleares. As microesferas implantadas no GI e GII mantiveram-se, em sua maioria, íntegras e envolvidas por tecido conjuntivo fibroso. Notou-se discreta neoformação óssea próxima às bordas e circunjacente a algumas microesferas. No GIII, a mineralização limitou-se às bordas e a área remanescente foi preenchida por tecido conjuntivo fibroso. Conclui-se que os biomateriais foram biocompatíveis, bioativos, osteocondutores e apresentaram biodegradação lenta, indicando seu grande potencial para em aplicações clínica como biomaterial de preenchimento.

Abstract The aim of this study was to analyze the biological behavior and osteogenic potential of magnesium (Mg) substituted hydroxyapatite (HA) microspheres, implanted in a critical bone defect, considering that this ion is of great clinical interest, since it is closely associated with homeostasis and bone mineralization. For the purpose of this study, 30 rats were used to compose three experimental groups: GI - bone defect filled with HA microspheres; GII - bone defect filled with HA microspheres replaced with Mg; GIII - empty bone defect; evaluated at biological points of 15 and 45 days. The histological results, at 15 days, showed, in all the groups, a discrete chronic inflammatory infiltrate; biomaterials intact and surrounded by connective tissue; and bone neoformation restricted to the borders. At 45 days, in the GI and GII groups, an inflammatory response of discrete granulomatous chronic type was observed, and in the GIII there was a scarce presence of mononuclear inflammatory cells; in GI and GII, the microspheres were seen to be either intact or fragmented, surrounded by fibrous connective tissue rich in blood vessels; and discrete bone neoformation near the edges and surrounding some microspheres. In GIII, the mineralization was limited to the borders and the remaining area was filled by fibrous connective tissue. It was concluded that the biomaterials were biocompatible and osteoconductive, and the percentage of Mg used as replacement ion in the HA did not favor a greater bone neoformation in relation to the HA without the metal.

Resumo Biomateriais compósitos têm ganhado notoriedade nas últimas décadas, devido à capacidade de combinar propriedades desejáveis de cada material. Assim, associar a bioatividade da wollastonita (W) com a biodegradabilidade do fosfato tricálcico (TCP) torna-se promissor para o reparo ósseo. Deste modo, este trabalho investigou, por meio de revisão sistemática e metanálise, estudos in vivo que avaliaram histomorfometricamente o reparo ósseo após implantação de compósitos de W/TCP. As buscas foram realizadas nas bases de dados PubMed/MEDLINE, LILACS/BIREME/Biblioteca Virtual em Saúde (BVS) e Scientific Electronic Library Online (SciELO). Dos 312 estudos encontrados, 6 foram incluídos. Na comparação dos dados considerou-se o percentual de neoformação óssea (NB). Compósitos com maior percentual de W e/ou no formato de arcabouços apresentaram maior NB. Estes resultados sugerem que a associação destes dois materiais bem como o formato de arcabouço poroso foram determinantes na NB, o que tornam estes novos compósitos profícuos para o uso clínico.

Abstract Composite biomaterials have gained notoriety in recent decades due to the ability to combine desirable properties of each material. Thus, associating bioactivity of wollastonite (W) with biodegradability of tricalcium phosphate (TCP) becomes promising for bone repair. Therefore, this study investigated, through systematic review and meta-analysis, in vivo studies that evaluated histomorphometrically the bone repair after implantation of W/TCP composites. The searches were performed in the PubMed/MEDLINE, LILACS/BIREME/Virtual Health Library (VHL), and Scientific Electronic Library Online (SciELO) databases. A total of 312 studies were identified in the databases, of which 6 were included. In data comparison, it was considered the percentage of neoformed bone (NB). Composites with a higher percentage of W and/or in the scaffold format presented higher NB. These results suggested that the association of these two materials, as well as the porous scaffold format, was determinant on NB, which makes these new composites potential for clinical use.

Resumo Objetivou-se avaliar novos biomateriais fosfatados para regeneração de defeito ósseo crítico. Distribuíram-se 45 ratos Wistar em três grupos: CON (sem implantação de biomaterial), FCB (grânulos de fosfato de cálcio bifásico: fosfato tricálcico tipo β, β-TCP/pirofosfato de cálcio) e FCB/BV (FCB/vidro bioativo fosfatado), avaliados aos 15, 45 e 120 dias de pós-operatório. No grupo CON, observaram-se neoformação óssea restrita às bordas ósseas e preenchimento do defeito por delgado tecido conjuntivo fibroso. Em FCB e FCB/BV, os grânulos preencheram toda a extensão do defeito e apresentaram maior fragmentação em FCB/BV. A neoformação óssea foi mais evidente no FCB. De permeio às partículas dos biomateriais formou-se um tecido conjuntivo frouxo, que evoluiu para fibroso em FCB. Os biomateriais desencadearam discreta reação inflamatória crônica granulomatosa, que se tornou inconspícua. Conclui-se que os materiais foram biocompatíveis, atuaram como arcabouços tridimensionais, apresentaram potencial osteocondutor e favoreceram a regeneração óssea, principalmente FCB. A adição do vidro bioativo aumentou a biodegradabilidade de FCB/BV.

Abstract The objective was to evaluate new phosphate biomaterials for the regeneration of a critical bone defect. 45 Wistar rats were distributed in three groups: CON (without biomaterial implantation), FCB (biphasic calcium phosphate granules: β-tricalcium phosphate, β-TCP/calcium pyrophosphate) and FCB/BV (FCB/bioactive glass granules), evaluated at 15, 45, and 120 postoperative days. In the CON group, bone neoformation restricted to bone edges and filling of the defect by thin fibrous connective tissue were observed. In FCB and FCB/BV, the granules filled the entire extent of the defect and showed greater fragmentation in FCB/BV. Bone neoformation was more evident in FCB. From the biomaterial particles, a loose connective tissue was formed, which evolved to fibrous in FCB. Biomaterials triggered a discrete chronic inflammatory granulomatous reaction, which became inconspicuous. It was concluded that materials were biocompatible, acted as three-dimensional scaffolds, presented osteoconductive potential, and favored bone regeneration, especially FCB. The addition of bioactive glass increased the biodegradability of FCB/BV.