The objective of this study is to evaluate the surface physicochemical properties of Ti6Al4V alloy after etching with a piranha’s solution at temperatures of 25 °C, 40 °C, and 60 °C for 30 min. Scanning electron microscopy with energy-dispersive X-ray spectroscopy, optical profilometry, X-ray diffraction, and wettability analyses were used to characterize the surface of the samples. In addition, corrosion tests were performed using potentiodynamic polarization and electrochemical impedance spectroscopy. The proposed surface treatment did not alter the wettability and surface chemistry (crystallinity), but the texture, surface roughness, superficial area, and corrosion resistance of the alloy could be changed by varying the etching temperature. Considering that these properties are indirect indicators of the alloy’s potential success in the osseointegration of a dental implant, the surface treatment of the Ti6Al4V alloy using a piranha solution while controlling the etching temperature has attractive biomedical applications.

Ni-Co ferrites, especially the ones with lower cobalt fractions, are candidate materials for applications in magnetomechanical sensors and electromagnetic wave absorbers. This work studied the microstructure, magnetostriction, flexural strength, and complex magnetic permeability of Ni0.9Co0.1Fe2O4, presenting data that weren't covered by previous literature on this composition. It was found that sieving the calcined powder before the forming operation increased the flexural strength of the ceramic. The Ni-Co ferrite had a saturation magnetostriction of 36ppm. The real part of the complex magnetic permeability varied between 2.2-2.3 in frequencies from 100MHz to 1GHz. In frequencies higher than 1GHz, µ' decreased sharply and reached 1 at 3.9GHz. It was found that the grinding media provided a small fraction of Al to the ferrite composition, which apparently affected the complex magnetic permeability of the material but the magnetostriction results were very close to Al-free Ni-Co ferrites with similar composition.

Titanium and its alloys have been used in dentistry to due their excellent corrosion resistance and biocompatibility. However, titanium coating is bioinert material and it cannot chemically bond to bone tissue. The purpose of this work was evaluating the bioactivity of Ti-7,5Mo alloy after chemical treatment using H2SO4 / H2O2 and soaking in SBF. Samples were chemically treated at room temperature for 4 h with a solution consisting of equal volumes of concentrated H2SO4 (200 ml) and 30% aqueous solution H2O2 (200 ml). The oxidized samples were rinsed with distilled water and were heat treated at 600°C for 1h in a electrical furnace in air. Then, all samples were immersed in SBF (Simulated Body Fluid) for 7 and 14 days to form a calcium phosphate (Ca/P) coating on the surface. Surfaces were characterized by using SEM, AFM and contact angle. The results indicated that calcium phosphate (Ca/P) was formed on surface of Ti-7.5Mo experimental alloy.

ABSTRACT: Mullite is an excellent structural material due to its high temperature stability, high electrical insulation capabilities and creep resistance. This material has a number of technological applications, such as rocket nozzles used in the aerospace industry. In this work, mullite was obtained by sol-gel process, using silicic sol, aluminum nitrate and ethylene glycol, besides the following volume ratios of silica sol dispersion to ethylene glycol: 1/0; 1/1; 1/2; and 1/3. After drying, the samples were thermal treated at temperatures of 1,000; 1,100; 1,200 and 1,250°C. The samples were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) and specific surface area (Bruner-Emmett-Teller - BET). SEM showed that mullite particles are fine and nearly equiaxed. The sample without ethylene glycol showed 3/2 mullite after heat treatment at 1,250°C. The sample with intermediate ethylene glycol concentration presented two crystallization processes: the first at 1,000°C forming mullite and spinel phases, and the second at 1,250°C forming only 3/2 mullite. However, the sample with the highest ethylene glycol concentration crystallized directly to mullite at 1,000°C with the highest yield. There is a strong dependence on the specific surface area with temperature. The Rietveld refinement showed that the a cell lattice of mullite and the Al/Si molar ratio in the mullite formula depend on the ethylene glycol presence and on the calcination temperature. The lattice parameters b and c are not dependent on the alumina content, but the parameter a increases with the increase in the alumina content. Samples prepared with higher ethylene glycol concentrations reached higher mullite yields at lower temperatures.

Ceramic cutting tools are showing a growing market perspective in terms of application on machining operations due to their high hardness, wear resistance, and machining without a cutting fluid, therefore are good candidates for cast iron and Nickel superalloys machining. The objective of the present paper was the development of Si3N4 based ceramic cutting insert, characterization of its physical and mechanical properties, and subsequent coating with AlCrN using a PVD method. The characterization of the coating was made using an optical profiler, XRD, AFM and microhardness tester. The results showed that the tool presented a fracture toughness of 6.43 MPa.m½ and hardness of 16 GPa. The hardness reached 31 GPa after coating. The machining tests showed a decrease on workpiece roughness when machining with coated insert, in comparison with the uncoated cutting tool. Probably this fact is related to hardness, roughness and topography of AlCrN.

The optimization of the energy generated by a MagnetoHydroDynamic (MHD) channel using a superconducting magnet demands the optimization of the magnetic field of the system and of the critical points on the magnet winding. This work must include the development of a high performance superconductor wire suitable for this system. Aiming to the construction of improved performance MHD channel, it was developed a low cost superconductor wire, with the required characteristics. The wire was made using a technology compatible with the assembling steps and heat treatment conditions of the MHD superconducting magnets fabrication. It was used the internal Sn method in Nb-7.5wt%Ta tube to fabricate a 271-filament wire with a diameter of 0.81 mm and a Cu/nonCu ratio of 2.3. The wire was heat treated at 200 °C to diffuse the Sn into the Cu shell, producing bronze, followed by the final reaction at temperatures ranging from 670 °C to 730 °C during 25 to 150 h, to produce (Nb,Ta)3Sn. The superconducting wire characterization was made measuring the critical current Ic versus the applied magnetic field in the range of 5 to 20 T, the critical temperature Tc and the residual resistivity ratio (RRR). The wire transported critical currents above those available in commercial superconducting wires. These values of Ic are higher than the expected values for the optimization of the MHD channel.