The silicon alkoxides-based coating is an alternative to control the release of cytotoxic ions through metal implants. This study evaluated the influence of the number of layers of a hybrid coating on the surface of austenitic stainless steel AISI 316L on the corrosion resistance. This coating was produced from the precursors of silicon alkoxides 3-(trimethoxysilyl)propyl methacrylate (MAP) and tetraethoxisylane (TEOS) obtained by sol-gel process, and easily applied by dip-coating. Results indicated that a single layer of coating in the substrate showed a better protection than two layers. This single layer developed by the combination of the precursors TEOS-MAP was enough to create a compact and uniform film with good adherence to AISI 316L and higher electrochemical development. A single layer of TEOS-MAP coating is more adequate as a protective coating for the AISI 361L than the sample subjected to two layers and the non-coated substrate, because this film ensures its integrity in an aggressive environment.

Abstract Coatings developed through sol-gel method is presented as an interesting replacement to chromium coating. Sol-gel method present advantages as high purity and excellent distribution of the components. The objective of this work is to synthesize and characterize a film obtained by sol-gel route. The film was prepared with 3-(trimethoxysilylpropyl) methacrylate (TMSPMA), tetraethoxysilane (TEOS) and cerium nitrate, using water and ethanol as solvents. Polyethyleneglycol (PEG) plasticizer was added at four different concentrations. The sol was characterized by techniques of viscosity, thermogravimetric analysis (TGA), X-ray diffraction (XRD) nuclear magnetic resonance spectroscopy (NMR) and Fourier transform infrared spectroscopy (FT-IR). The results showed that tetrafunctional alkoxides condensation was retarded by the plasticizer, forming a compact film. The film with 20 g.L-1 of PEG showed the best electrochemical behavior.

The epoxy resin is one of the matrices most employed in obtaining composites and coatings. Its properties have been modified using materials such as clays and polyhedral oligomeric silsesquioxanes - POSS. The use of POSS in the preparation of thermosetting nanocomposites has been studied in obtaining hybrid materials with higher mechanic and surface properties. The functionality of POSS cage is important, since a thermosetting is formed by a cross-linked structure that can interact at any direction, forming bonds or acting in the interface of the cages inserted. This works aims to evaluate the influence of three POSS (Glycidylisobutyl-POSS, Triglycidylisobutyl-POSS and Glycidyl-POSS) added in epoxy resin, in the mechanic and electrochemical behaviors, when applied on low alloy steel. It was observed an increase in roughness and hydrophobicity. The sample containing Glycidylisobutyl-POSS presented the best results of corrosion resistance. Glycidyl-POSS showed an inefficient dispersion, forming agglomerates, leading to a low electrochemical behavior.

Siloxane-poly(methyl methacrylate) (PMMA) organic-inorganic hybrid coatings were deposited on galvanized steel by the dip-coating sol-gel technique. Anticorrosion properties, as well as the morphological, surface and structural features were studied. Hybrid coatings were synthesized from tetraethoxy-silane (TEOS) and methyl methacrylate (MMA) as inorganic and organic phases, respectively, linked by 3-metacriloxypropyl-trimethoxysilane (TMSM) as a coupling agent. The MMA/TMSM ratio was kept constant, whereas the four TEOS/TMSM ratios were varied. The characterization of coatings was assessed using several techniques such as Scanning Electronic Microscopy (SEM), Contact Angle, Fourier Transform Infrared (FT-IR), Open Circuit Polarization (OCP), Atomic Force Microscopy (AFM) and Electrochemical Impedance Spectroscopy measurements (EIS). The EIS results, which were obtained for the hybrid coatings, were discussed based on an electrical equivalent circuit used to adjust the experimental data. The results showed that the increasing the TEOS content caused increase in coating thickness, increased in the surface roughness and increased in the surface hydrophobicity. The film with the highest TEOS content presented the best electrochemical performance, more effective in protecting against corrosion.