A kind of corrosion-resistant Ni-Mo-P composite coating was deposited on the surface of AZ91D magnesium alloy substrate by electroless plating method with different concentration of Ce(NO3)3 and Nd(NO3)3. The deposition mechanism of Ni-Mo-P composite coating was explored. Furthermore, the effects of Ce(NO3)3 and Nd(NO3)3 concentration on the microstructure and properties of Ni-Mo-P composite coatings were studied. Results indicated that the Ni-Mo-P composite coatings prepared by adding the optimal concentration of Ce(NO3)3 and Nd(NO3)3 had few defects. Meanwhile, the deposition rate of the composite coatings and the adhesion between the coating and the magnesium alloy substrate were improved. When the concentration of Ce(NO3)3 and Nd(NO3)3 were 0.10 and 1.00 g/L, the Ni-Mo-P composite coatings had the minimum corrosion rate of 0.826 and 0.681 g/m2·h, respectively. Herein, compared with the addition of Ce(NO3)3, the Nd(NO3)3 added Ni-Mo-P composite coating has the maximum arc radius of capacitive resistance and significant improvement corrosion resistance.

Abstract Ni-W-P ternary coating was successfully deposited on AZ91D magnesium alloy by electroless plating with low energy consumption. The effect of Na2WO4 concentration on the microstructure, deposition rate, corrosion behavior, adhesion force, porosity test and micro-hardness of Ni-W-P ternary coatings were evaluated. Results reveal that when the concentration of Na2WO4 is 15 g/L in the plating solution, the coating with the average thickness of 17 μm is uniform and dense, and the content of phosphorus and tungsten reached 9.63 wt.% and 1.14 wt.% respectively, which presents amorphous structure. Meanwhile, when the concentration of Na2WO4 is 15 g/L, the amorphous Ni-W-P ternary coating has the best corrosion resistance, among which Ecorr is -0.326 V, Icorr is 0.003 A/cm2 in 3.5 wt.% NaCl solution. In addition, the mechanisms of corrosion resistance for the substrate and the coating were exploded.

Abstract Ni-Co-Al2O3-MoS2 composite coatings were prepared on the surface of LY12 aluminum alloys by electrophoresis-electrodeposition with different MoS2 concentrations. The microstructure, morphologies and composition of Ni-Co-Al2O3-MoS2 composites were characterized by X-ray diffractometer (XRD) and scanning electron microscopy (SEM) equipped with energy dispersive spectroscope (EDS). The micro-indentation hardness as well as friction and tribological properties of the coatings were tested by micro-hardness tester and friction and wear tester separately. Results revealed that the composite coating fabricated at 1.0 g⋅L-1 MoS2 achieved dense structure, and the average thickness of the coating was 39.820 µm. The micro-indentation hardness of the composite coating was decreased from 578 HV to 465 HV with the increase of MoS2 concentration. Also, the composite coating synthesized at 1.0 g·L-1 MoS2 had the lowest friction coefficient and wear rate.