This work reports on the properties of GaN films grown by reactive magnetron sputtering onto glass substrate kept at relatively low temperature (400°C), using different RF power applied to the Ga target. Their structural, morphological, vibrational and optical properties were characterized by X-ray diffraction, atomic force and scanning electron microscopies, Raman spectroscopy and UV-vis spectrophotometry. The films have wurtzite phase with strong preferential orientation in the c-axis direction. Moreover, two clear contributions to the (0002) diffraction peak could be found, indicating the presence of two different morphologies, which were discussed in terms of the formation of an intermediate layer between the substrate and a dominating columnar-like microstructured film.

Abstract This work reports the properties of GaN films grown onto c-Si (100) at relatively low substrate temperature (400°C) by reactive magnetron sputtering. The study depicts the effect of working pressure and RF power on the GaN film structural, vibrational and optical properties characterized by X-ray diffraction, atomic force and scanning electron microscopies, Raman spectroscopy and spectroscopic ellipsometry. Unusual low pressure deposition condition (0.40 Pa) was achieved by using a separated argon inlet directed to the Ga target surface, resulting in improved crystalline quality of the films. In this condition, the preferential crystalline orientation, the surface morphology and the optical gap of the GaN films show a strong dependence on the RF power applied to the Ga target, where low RF power (30-60 W) was responsible for increasing the c-axis orientation and the optical gap, while higher RF power (75-90 W) decreased the overall crystal quality and increased the surface roughness.