Abstract Over the years, the demand for high engine efficiency has resulted in the development of new generation superalloys with improved elevated temperature properties, especially creep resistance. This study aimed to evaluate creep and mechanical behavior of Inconel 718 superalloy. Creep tests were performed at temperature range of 650 to 700 °C and stress range of 625 to 814 MPa. Hot tensile and oxidation tests were performed and the characterization techniques used in this study were scanning electron microscopy (SEM) for microstructural and fracture surface analysis, transmission electron microscopy (TEM) for precipitates analysis; grazing X-ray diffraction for analysis of oxide formation and Vickers microhardness. The analyze of stress exponent value (n = 36.48) and activation energy (Qc = 512.97 kJ/mol), suggested that creep mechanism at 650 °C was the climb dislocation mechanism. The Inconel 718 presented ductile fracture at 650 and 700 °C and intergranular fracture to 675 °C.

Metals solidification involves the transformation of the molten metal back into the solid state. Solidification structures impact heavily on the final product's characteristics. The microstructure effects on metallic alloys properties have been highlighted in various studies and particularly the dendrite arm spacing influence upon the mechanical properties such as tensile strength has been reported. In the present investigation, Al-10wt%Si-2wt%Cu and Al-10wt%Si-5wt%Cu alloys were directionally solidified upward under transient heat flow conditions. The experimental results include solidification thermal parameters such as tip growth rate and cooling rate, optical microscopy, volume fraction of the eutectic mixture, primary dendritic arm spacing and ultimate tensile strength. Experimental growth laws of primary dendrite arm spacing as a function of the solidification thermal parameters are proposed. The Hall-Petch mathematical expressions were used to correlate the ultimate tensile strength as a function of the primary dendritic arm spacing. It was found that the alloy with higher copper content had a more refined structure. More refined structures had higher ultimate tensile strength values.

Plasma nitriding of a solution annealed and aged 300 grade maraging steel was studied aiming to increase the creep resistance. The surface microhardness reached 1,140 HV, producing 50 µm layer composed of ε-Fe3N and γ'-Fe4N nitrides at the uppermost sample layer. The inner core remained unaltered presenting typical plate-like martensite microstructure of maraging steels with average microhardness of 604 HV. Surface RMS roughness in the nanometric scale increase from 52 nm to 71 nm. The continuous layer of iron nitrides seems to behave as a barrier for oxidation and for inward oxygen diffusion improving the creep resistance by reducing the steady-state creep rate (εs) in 52-65% when compared with the literature results. Dominant creep mechanism is controlled by dislocations climb. Fracture surfaces of specimens presented ductile failure consisting of equiaxed and bi-modal dimples in the fibrous zone surrounded by 45º shear lip. Nitrided sample presented a reduced ductility, associated to the hard surface layer.

Biomaterials (composites and blends) play a major role in the health of modern society. This paper reports on the preparation and characterization of polyvinylidene fluoride (PVDF) and hydroxyapatite (HAP) composites, analyzing the incorporation of HAP in PVDF and investigating their mechanical properties and cytotoxicity (biocompatibility) for use in bone restoration and filling. The material was prepared in film form by the casting method. PVDF pellets were dissolved in dimethylacetamide (DMA), a HAP/DMA emulsion was prepared. The materials were mixed in proportions of 100/00, 90/10, 80/20, 70/30, 60/40, 50/50, 40/60, 30/70 in weight and left to dry in an oven, resulting in homogeneous, flexible films which were characterized by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), X ray diffractometry (XRD), contact angle measurement, and by mechanical and cytotoxicity tests.