Geometry and electronic structure of chiral carbon and carbon nitride (CNx) nanotubes were investigated through quantum chemical methods. Finite nanotubes with diameters ranging from 5 to 10 Å and containing up to 500 atoms were considered. CNx structures were built through random substitution of carbon atoms by nitrogen. The molecules were fully optimized by semi-empirical quantum chemical method (PM3). Our results show that the energy associated with nitrogen incorporation depends strongly upon the tube helicity and diameter. The doping of nanotubes with nitrogen contributes to reduce the stress caused by the small diameter of the studied systems. Density of States (DOS) results for pure carbon and CNx nanostructures, obtained through DFT and Hartree-Fock calculations, were analyzed. The introduction of nitrogen in the tube produce states in the gap region which characterizes the metallic behavior, as expected for these systems after N-doping.

Theoretical analysis of formation energy and geometry was done to compare the relative stabilities of modified carbon nanostructures representative fragments. Structure and energies of formation were calculated at semiempirical level of theory. Depending of B-N pair localization on the molecular structures the formation enthalpy decreases. B-N substitution in tubular structures at low concentration decreases the energy when the tubes have small diameters. Our results are in according to experimental works which have shown that boron and nitrogen are met at region of defects in B X C Y N Z nanostructures.